A.升色溫波璃性
牌 號
|
厚度
(mm) |
A[2856k]
|
D65
|
化學穩定性
|
ND
|
α×10-7
(/℃) |
Tg
(℃) |
Ts
(℃) |
S
|
|||||
x
|
y
|
Y
|
x
|
y
|
Y
|
DA
|
DW
|
|||||||
SSB40
|
2
|
0.415
|
0.403
|
63.0
|
0.283
|
0.305
|
64.1
|
2
|
4
|
1.521
|
87
|
585
|
638
|
2.58
|
SSB130
|
2
|
0.358
|
0.399
|
36.3
|
0.242
|
0.277
|
39.4
|
2
|
4
|
1.521
|
102
|
602
|
672
|
2.57
|
SSB145
|
2
|
0.361
|
0.372
|
22.1
|
0.239
|
0.243
|
23.7
|
2
|
4
|
1.521
|
87
|
585
|
638
|
2.58
|
升色溫玻璃技術要求
牌 號
|
厚 度(mm)
|
υ(Mired)
|
|
標準
|
公差
|
||
SSB40
|
2
|
-40
|
-40±4
|
SSB130
|
2
|
-130
|
-130±13
|
SSB145
|
2
|
-145
|
-145±14.5
|
升色溫玻璃氣泡、條紋、應力類級別
牌 號
|
氣 泡
|
條 紋
|
應 力
|
SSB40
|
C
|
3C
|
3
|
SSB130
|
C
|
3C
|
3
|
SSB145
|
C
|
3C
|
3
|
牌 號
|
厚度
(mm) |
A[2856k]
|
D65
|
化學穩定性
|
ND
|
α×10-7
(/℃) |
Tg
(℃) |
Ts
(℃) |
S
|
|||||
x
|
y
|
Y
|
x
|
y
|
Y
|
DA
|
DW
|
|||||||
SSB165
|
2
|
0.340
|
0.360
|
15.4
|
0.227
|
0.224
|
16.9
|
2
|
4
|
1.521
|
87
|
585
|
638
|
2.58
|
SSB200
|
2
|
0.318
|
0.348
|
10.1
|
0.214
|
0.209
|
11.4
|
2
|
4
|
1.521
|
87
|
585
|
638
|
2.58
|
牌 號
|
厚 度(mm)
|
υ(Mired)
|
|
標準
|
公差
|
||
SSB165
|
2
|
-165
|
-165±16.5
|
SSB200
|
2
|
-200
|
-200±20
|
牌 號
|
氣 泡
|
條 紋
|
應 力
|
SSB165
|
C
|
3C
|
3
|
SSB200
|
C
|
3C
|
3
|
寧波振華光電公司技術薄膜不足總部于200半年設立,有的是家專業課程光電公司技術薄膜組件產出方式商,分為所有有色金屬窗破璃濾光片、透紫外線窗破璃、透紅外窗破璃、光電公司技術薄膜渡膜窗破璃、帶通濾光片、隔音窗破璃、熔融石英窗破璃、高硼硅窗破璃、高鋁硅窗破璃、K9窗破璃、B270窗破璃、耐福射窗破璃、防福射窗破璃、微晶窗破璃、光柵、碼盤、偏振片、三菱鏡、透鏡、濾色鏡、紅外發送二級管、光敏三級管、硅光電公司技術薄膜池、乳白窗破璃成功研制、制作產出方式所有與眾不同標準品種的濾光片、照象機濾色鏡、透鏡、三菱鏡等所有光電公司技術薄膜組件。